RIE 1200

Dry Film Lubricant

GENERAL DESCRIPTION

RIE 1200 prevents corrosion, galling, seizing, and fretting.  It is a low friction coating which exhibits long wear life when operated at  -320° F to + 500° F under loads exceeding 100,000 psi.

            RIE 1200 should be applied where maximum wear life and corrosion protection are required.   

RECOMMENDED USAGE

            *  Where permanent lubrication is desired.

            *  Where "clean operation" is desired (RIE 1200 will not collect dirt and debris as do grease and oils).

            *  Where parts may be subjected to frequent disassembly.

            *  Where a protective coating and sacrificial break-in-lubricant is needed.

            *  Where fretting and galling is a problem  (such as splines, universal joints and keyed bearings).

*  Where easy release is desired (such as acme nuts and stainless steel screws).

   PHYSICAL PROPERTIES

            Vehicle Type .........……….                Epoxy-Phenolic

            Lubricative Pigment...…….                  Inhibited molybdenum disulfide

            Color ................………….                 Flat Dark Gray

Film Thickness .......………                  .2 - .8 mils depending on properties desired

Operating Temp. Range…..                  -320° F to +500° F    

            Military Spec.................……..             MIL-L-8937D

            Vacuum Out Gassing …………           None @ 10³  Torr.

            Lox Compatibility……………             100% Compatible and shock resistant

            Wear Life…………………….            500-900 minutes depending on surface preparation

                                                                        (Falex @ 1000 Lbs. Gauge load).

Load Carrying

            Capacity..........………………            2750 Lbs (Flex E.P.)

Corrosion Protection .………              Approximately 500 hours (5% salt fog @.0005"

                                                                        film thickness over zinc phosphate steel).